Monarch Coating Pvt. Ltd.

High build two component high solid acrylic polyurethane coating Offers excellent resistance to atmospheric exposure conditions Resistance to water and saline atmosphere splash and spillage of mild chemicals Gives tough and abrasion resistant finish on curing

GLO-PROTEK HS ALIPHATIC ACRYLIC PU-612High Solid Aliphatic Acrylic base Polyurethane Top Coat with High GlosGlo-Protek HS Aliphatic Acrylic PU-612 coating is developed using high solids polyurethane with N75 hardener of Bayer. The coating is thin film and has very high abrasion resistance, excellent UV resistance properties and resistance to chemical fumes exposure.
SURFACE PREPARATION :Surfaces must be clean and dry. Dirt, dust oil and other contaminants should be removed. A suitable primer for concrete or steel application from our range may be used as per instruction of the company
PERFORMANCE DATA :Abrasion on concrete One coat of paint @ 50 microns after primer 70 mg. loss after 1000 cycles, CS17 wheel, 1000 gm. load
WATER / SALT WATER RESISTANCE :No rusting, no blistering, softening or discoloration after either 30 days of fresh water Immersion or 30 days of saltwater immersion at 35 Deg C.
SOLIDS CONTENT :60% by weight
THEORETICAL COVERAGE RATE :VOC Values : 8 sqm / coat @ 50 microns by brush.Excellent flow characteristics allow for application by spray or roller.Superior impact and abrasion resistance and can be relocated.
COLOUR SHADE AND PACKING :All Ral shades - 2 kg and 5 kg and custom built kits.
STORAGE :Six months from the date of manufacture.Store under cool, dry & sheltered place away from direct sunlight, heat & water.

GLO-PROTECT HIGH BUILT ACRYLIC PU FINISHGlo-Protek High Built Acrylic PU Finish is a two pack Polyurethane Finish Coating based on Acrylic Aliphatic Isocyanate Adduct
SUGGESTED USESAn ideal coating to be used as a topcoat over an epoxy base coat or in a total polyurethane painting scheme. The cured film provides hard, flexible, abrasion resistant coating which has excellent weatherability, gloss and colour retention and is resistant to humidity, saline and a variety of chemically polluted environment.